Thermal Ceramics, Inc.
Augusta, GA 30903
Feb 04, 2008 Kaolite 2000-LI can be gunned or pumped into place for high temperature industrial processes. With its low iron oxide content, product can be used in carburizing furnaces or where high concentrations of CO gas are present. Strength-to-density ratio ranges from 11 to 12 psi/pcf. Low k values along with high cold crushing strengths of 450 psi at densities of 38-41 pcf provides insulation and thermal efficiency to reduce energy costs.

Thermal Ceramics, Inc.
Augusta, GA 30903
Apr 06, 2005 Offering quality control from raw material specifications to manufacturing process, Kaolite 1:2:4 is tested by outside testing lab for standard quality conformance. Product, which can be gun or cast, is comprised of 1 part Lumnite or other mid-grade calcium aluminate cement; 2 parts haydite, expanded shale; and 4 parts vermiculite. Physical properties include 48–56 lb/ft³ density and 400–500 psi crushing strength, after firing at 1,500°F.